ABSTRACT
Cobalt (III) oxide (Co3O4) thin films were deposited on glass substrates at a temperature of
70°C with continuous stirring and heating of the alkaline bath of various pH of 8, 10, 12 and
14. Cobalt (II) chloride hexahydrate (CoCl2·6H2O) was used as source of Co2+ and to make it
alkaline, 25% aqueous ammonia solution was added as the complexing agent with constant
heating and stirring. The bath was doped with zinc nitrate (Zn(NO3)2 and later, some samples
were annealed at 200°C for 30 minutes. X-ray diffraction method was used to confirm the
depositions. The structural features obtained from the x-ray diffraction showed the peaks of
Co3O4 and increase in crystallinity as pH increases which was confirmed by SEM. It also
shown improvement in crystallinity after doping and annealing. The optical studies showed a
variation of absorbance, reflectance, direct band gap energy and refractive index as pH varies
and changes after doping and annealing. The range of direct band gap energy and refractive
index obtained are 1.34eV - 2.85eV and 1.38 - 2.07 respectively. The values of the band gap
energy and refractive index obtained indicate possible applications in photovoltaic systems,
optoelectronics, laser diodes and light emitting diodes.
MMADUKA, O (2021). Influence Of Ph, Doping And Annealing On Structural And Optical Properties Of Chemical Bath Deposited Cobalt (Iii) Oxide (Co3o4) Thin Films. Afribary. Retrieved from https://tracking.afribary.com/works/influence-of-ph-doping-and-annealing-on-structural-and-optical-properties-of-chemical-bath-deposited-cobalt-iii-oxide-co3o4-thin-films
MMADUKA, OBODO "Influence Of Ph, Doping And Annealing On Structural And Optical Properties Of Chemical Bath Deposited Cobalt (Iii) Oxide (Co3o4) Thin Films" Afribary. Afribary, 13 May. 2021, https://tracking.afribary.com/works/influence-of-ph-doping-and-annealing-on-structural-and-optical-properties-of-chemical-bath-deposited-cobalt-iii-oxide-co3o4-thin-films. Accessed 23 Nov. 2024.
MMADUKA, OBODO . "Influence Of Ph, Doping And Annealing On Structural And Optical Properties Of Chemical Bath Deposited Cobalt (Iii) Oxide (Co3o4) Thin Films". Afribary, Afribary, 13 May. 2021. Web. 23 Nov. 2024. < https://tracking.afribary.com/works/influence-of-ph-doping-and-annealing-on-structural-and-optical-properties-of-chemical-bath-deposited-cobalt-iii-oxide-co3o4-thin-films >.
MMADUKA, OBODO . "Influence Of Ph, Doping And Annealing On Structural And Optical Properties Of Chemical Bath Deposited Cobalt (Iii) Oxide (Co3o4) Thin Films" Afribary (2021). Accessed November 23, 2024. https://tracking.afribary.com/works/influence-of-ph-doping-and-annealing-on-structural-and-optical-properties-of-chemical-bath-deposited-cobalt-iii-oxide-co3o4-thin-films