STRESS LOOP EFFECTS IN DUCTILE FAILURE OF MILD STEEL

ABSTRACT

A simulation study of effect of stress on mild steel microstructure has revealed stress loop at areas of stress application which are believed to be the root cause of ductile failure morphology in ductile alloys under plane strain conditions.

Overall Rating

0

5 Star
(0)
4 Star
(0)
3 Star
(0)
2 Star
(0)
1 Star
(0)
APA

Oluwole, O (2021). STRESS LOOP EFFECTS IN DUCTILE FAILURE OF MILD STEEL. Afribary. Retrieved from https://tracking.afribary.com/works/stress-loop-effects-in-ductile-failure-of-mild-steel

MLA 8th

Oluwole, O "STRESS LOOP EFFECTS IN DUCTILE FAILURE OF MILD STEEL" Afribary. Afribary, 01 Apr. 2021, https://tracking.afribary.com/works/stress-loop-effects-in-ductile-failure-of-mild-steel. Accessed 23 Nov. 2024.

MLA7

Oluwole, O . "STRESS LOOP EFFECTS IN DUCTILE FAILURE OF MILD STEEL". Afribary, Afribary, 01 Apr. 2021. Web. 23 Nov. 2024. < https://tracking.afribary.com/works/stress-loop-effects-in-ductile-failure-of-mild-steel >.

Chicago

Oluwole, O . "STRESS LOOP EFFECTS IN DUCTILE FAILURE OF MILD STEEL" Afribary (2021). Accessed November 23, 2024. https://tracking.afribary.com/works/stress-loop-effects-in-ductile-failure-of-mild-steel